| Title: | Gd_1+xBa_2-xCu_3O_7-y溶融バルク超伝導体の作製と超伝導特性 |
| Other Titles: | Gd_1+xBa_2-xCu_3O_7-y ヨウカイ バルク チョウデンドウタイ ノ サクセイ ト チョウデンドウ トクセイ
Preparation and Superconducting Properties of Melt-textured Gd_1+xBa_2-xCu_3O_7-y Bulk Superconductor |
| Authors: | 高木, 淳
藤澤, 良雄
TAKAGI, Atsushi
FUJISAWA, Yoshio |
| Issue Date: | 31-Mar-2007 |
| Publisher: | 愛知工業大学 |
| Abstract: | the Gd＋Ba－Cuo (Gd123) bulk superconductor was prepared through the so-called MMTG process in the air. The superconducting transition temperature T for the sample subjected to post-annealing in oxygen atmosphere was 94K. The critical current Density J was determined to be 50000A/cm at 77k and 0T. The maximum trapped magnetic flux density has reached 0.51T at 77K at the enter of sample surface, which is approximately twice as large as the same-sized YBCuO (Y123) bulk sample. |