Title: 熱分解炭素を被覆したカーボンビーズのリチウムイオン電池負極特性
Other Titles: ネツ ブンカイ タンソ ヲ ヒフク シタ カーボン ビーズ ノ リチウム イオン デンチ フキョク トクセイ
Carbon beads Coated with pyrolytic Carbon and Their Anode Properties for Lithium-ion Battery
Authors: 大澤, 善美
中島, 剛
OZAWA, Yoshimi
NAKAJIMA, Tsuyoshi
Issue Date: 24-Sep-2009
Publisher: 愛知工業大学
Abstract: Using the pressure-pulsed chemical vapor infiltration technique,thin pyrocarbon films were coated on the surface of the hard-carbon particles. The crystallinity of pyrocarbon shell was higher than that of the core carbon. The BET surface area and the pores with the diameter of 1.5-5 nm were extremely decreased after coating with 7 wt% pyrocarbon. These changes in the nano-scaled structure of carbon surface could lead to the reduction of irreversible capacity. The cycleability was improved by pyrocarbon-coating,which would be attributed to the increase of the surface roughness on sub-micron scale by coating with the pebble-like pyrocarbon film to increase the adhesion among the particles by the organic binders.
URI: http://hdl.handle.net/11133/1692
Appears in Collections:11号

Files in This Item:

File Description SizeFormat
総研11号(P33-36).pdf800.1 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback